    不銹鋼彈簧表面堿性氧化處理注意須知
    文章來源:http://www.tlwpp.com/ 發布時間:2022-06-11 瀏覽次數:
    為提高氧化膜的耐腐蝕性,通常將不銹鋼彈簧浸入肥皂或重鉻酸鹽溶液中填充或鈍化氧化膜的孔隙,然后使用機油、主軸油、變壓器油等。.坑被填滿了。不銹鋼彈簧通常用5%-10%的皂液處理,溫度80-90℃,時間3-5min。也可用重鉻酸鉀質量分數為3%~5%的溶液處理,溫度90-95℃,時間10-15min。
    In order to improve the corrosion resistance of the oxide film, stainless steel springs are usually immersed in soap or dichromate solution to fill or passivate the pores of the oxide film, and then oil, main shaft oil, transformer oil, etc. are used The pit was filled. Stainless steel springs are usually treated with 5%-10% soap solution at 80-90 ℃ for 3-5min. It can also be treated with potassium dichromate solution with mass fraction of 3% ~ 5%, temperature 90-95 ℃, time 10-15min.
    鈍化或皂化后的泉水需要用溫水清洗,曬干或曬干,然后在105-110℃的錠子油中浸泡5-10分鐘,取出靜置10-15分鐘,使殘留表面的油流出。進行氧化處理時,為保證表面質量,應注意以下事項:
    The passivated or saponified spring water needs to be washed with warm water, dried in the sun or in the sun, and then soaked in spindle oil at 105-110 ℃ for 5-10 minutes. Take it out and stand for 10-15 minutes to make the oil on the residual surface flow out. During oxidation treatment, the following items shall be noted to ensure surface quality:
    1)彈簧氧化前,必須清除表面油污、氧化皮和熱處理鹽殘留物。
    1) Before the spring is oxidized, the oil stain, oxide skin and heat treatment salt residue on the surface must be removed.
    2)彈簧表面的接觸鍍銅層必須在除銅槽內清除干凈后才能進入氧化槽。
    2) The contact copper coating on the spring surface must be cleaned in the copper removal tank before entering the oxidation tank.
    3)銅及銅合金彈簧不能進入氧化槽。
    3) Copper and copper alloy springs shall not enter the oxidation tank.
    4)用于氧化處理的吊籃或吊鉤不得采用銅及銅合金材料,也不得采用釬焊。
    4) The hanging basket or hook used for oxidation treatment shall not be made of copper or copper alloy, nor shall it be brazed.
    不銹鋼彈簧
    5)浸油前必須用專用的浸油籃更換彈簧,并應檢查合格,確認彈簧合格后再浸油。
    5) Before oil immersion, the spring must be replaced with a special oil immersion basket, and it shall be inspected to be qualified. After confirming that the spring is qualified, oil immersion can be carried out.
    6)為使彈簧表面的氧化膜均勻,如有可能,應將彈簧按一定規則裝入籃中(建議垂直位置),或在氧化過程中,籃應在換籃槽內倒置1-2次,從而消除彈簧相互接觸處無氧化膜或氧化膜極薄的缺點。
    6) In order to make the oxide film on the spring surface uniform, if possible, the spring should be installed into the basket according to certain rules (vertical position is recommended), or during the oxidation process, the basket should be inverted in the basket changing groove for 1-2 times, so as to eliminate the defect that there is no oxide film or the oxide film is very thin at the contact between the springs.
    7)油浸槽應在規定的油溫下進行,待泡沫基本消除后才能拆下油槽。
    7) The oil immersion tank shall be carried out under the specified oil temperature, and the oil tank can be removed only after the foam is basically eliminated.
    8)皂化罐中應及時加入肥皂,注意不要將溶液煮沸,以免溢出罐。
    8) Soap should be added to the saponification tank in time. Be careful not to boil the solution to avoid overflowing the tank.
    9)清洗水建議是流動的水,液位要保持穩定,并在規定的時間換水。
    9) It is recommended that the cleaning water should be flowing water, the liquid level should be kept stable, and the water should be changed at the specified time.
    以上就是今天所要講解的內容了,相信大家在看完本文的描述之后,能夠對該產品有一定的認識和了解,希望以上內容能幫助到你。另外,若你想要了解更多相關資訊,可以多多關注我們的網站動態www.tlwpp.com。
    The above is the content to be explained today. I believe that after reading the description of this article, you can have a certain understanding of the product. I hope the above content can help you. In addition, if you want to learn more about our website, you can pay more attention to our website at www.sdzbthc com。